Permanent superhydrophobic polypropylene nanocomposite coatings by a simple one-step dipping process

CINTIA CONTRERAS; GABRIELA CHAGAS; MIRIAM STRUMIA; DANIEL WEIBEL

ELSEVIER SCIENCE BV

Lugar: Amsterdam; Año: 2014 vol. 307 p. 234 - 234

uperhydrophobic nanocomposite coatings on injection-molded polypropylene (PP) samples were prepared by dipping in xylene solvent containing titanium dioxide nanoparticles (NPs) functionalized with trimethoxypropyl silane. Alternatively, PP samples were dipped in a mixture of functionalized NPs and dissolved PP pellets. As a general result, dip-coated PP samples reached a permanent superhydrophobic state with a contact angle hysteresis (CAH) depending on NPs concentration and surface chemistry. SEM and profilometer measurements show a general trend in the decrease of CAH with the increase of aggregates and roughness. However some results showed that surfaces with the same roughness presented different CAHs. XPS measurements showed that low CAHs and self-cleaning properties were obtained only when the Ti?OH relative concentration on the surface was about 20%. At higher Ti?OH relative concentrations, the surface kept a superhydrophobic static state but lost its self-cleaning pro